Co Efficient of Thermal Expansion | ||
30-350°C | 10-6/°C | 4.8 |
30-400°C | 10-6/°C | 7.5 |
Density | g/cm³ | 8.13 |
Curie Temp | °F | 446 |
°C | 230 | |
Melting Point | °F | 2462 |
°C | 1450 | |
Modulus of Elasticity at 20°C | MPa | 145000 |
Youngs / Shears Modulus | MPa | 57000 |
Specific Heat at 20°C | J/g- °C | 0.51 |
Thermal Conductivity at 20°C | J/cm.s.°C | 0.105 |
Poisson's coefficient | 0.25 |
Sort | Grade | Chemical Composition (%) | ||||||||||
C≤ | P≤ | S≤ | Mn | Si | Ni | Cr | Co | Mo | Cu | Fe | ||
High magneticconductivity | 1J46 | 0.03 | 0.020 | 0.02 | 0.60~1.1 | 0.15~0.3 | 45.0~46.5 | ≤0.20 | Balance | |||
1J50 | 0.30~0.6 | 0.15~0.3 | 49.0~50.5 | ≤0.20 | ||||||||
1J77 | 0.03 | 0.020 | 0.02 | 0.30~0.60 | 0.15~0.3 | 75.0~78 | 3.9~4.5 | 4.80~6 | ||||
1J76 | 0.30~0.60 | 0.15~0.3 | 75.0~76.5 | 1.80~2.2 | 4.80~5.2 | |||||||
High initialpermeabilityof soft magnetic alloy | 1J79 | 0.60~1.1 | 0.30~0.50 | 78.5~80.0 | 3.80~4.10 | ≤0.20 | ||||||
1J80 | 0.60~1.1 | 1.10~1.5 | 79.0~81.0 | 2.6~3.0 | ≤0.20 | |||||||
1J85 | 0.30~0.60 | 0.15~0.3 | 79.0~81.0 | 4.80~5.20 | ≤0.20 | |||||||
1J86 | ≤1.00 | ≤0.30 | 80.5~81.5 | 5.80~6.2 |